| Creep Relaxation ASTM F38B (1/32”) |
40% |
|
| Sealability ASTM F37A (1/32”) |
.30 ml/hr |
|
| Klinger Hot Compression Test |
|
| Thickness Decrease 73°F (23°C) |
7% initial |
| Thickness Decrease 572°F (300°C) |
14% additional |
|
| Compressibility ASTM F36J |
7-17% |
| Recovery ASTM F36J |
55% minimum |
|
| Tensile Strength |
|
| ASTM F152 Cross Grain |
1,500 psi typical |
|
| Change in Tensile Strength |
|
| ASTM F152 after immersion in |
N/A |
| ASTM Oil IRM903, 5h/300°F (149°C) |
|
|
| Weight Increase |
|
| ASTM F146 after immersion in Fuel B |
N/A |
| 5h/73°F (23°C) |
|
|
| Thickness Increase |
Acid Resistance thickness increases |
| ASTM F146 after immersion in |
after immersion in: |
| ASTM Oil 1, 5h/300°F (149°C) |
50% Nitric Acid, 1hr/150°F 8% |
| ASTM Oil IRM903, 5h/300°F (149°C) |
96% Sulfuric Acid, 18hr/73°F 10% |
| ASTM Fuel A, 5h/73°F (23°C) |
65% Sulfuric Acid, 48hr/73°F 8% |
| ASTM Fuel B, 5h/73°F (23°C) |
>93% Nitric Acid Not Suitable |
|
| ASTM F104 Line Call Out |
F712000B6E00M5 |
|
| Leachable Chloride Content |
|
| FSA NMG-202-96 (Typical) |
N/A |
|
| Density |
100 lb/ft3 (1.6 g/cc) |
|
| Color (Top/Bottom) |
Off White |
|
Pressure and Temperature
Graphs
Material Thickness: 1/16”
Liquids |
 |
| Gases and Steam |
 |