| Creep Relaxation ASTM F38B (0.040”) |
20% |
|
| Sealability ASTM F37A (0.040”) |
.50 ml/hr |
|
| Klinger Hot Compression Test |
|
| Thickness Decrease 73°F (23°C) |
8% initial |
| Thickness Decrease 572°F (300°C) |
6% additional |
|
| Compressibility ASTM F36J |
7-17% |
| Recovery ASTM F36J |
50% minimum |
|
| Tensile Strength |
|
| ASTM F152 Cross Grain |
6,000 psi typical (4,000 psi with grain) |
|
| Change in Tensile Strength |
|
| ASTM F152 after immersion in |
15% |
| ASTM Oil IRM903, 5h/300°F (149°C) |
|
|
| Weight Increase |
|
| ASTM F146 after immersion in Fuel B |
10% |
| 5h/73°F (23°C) |
|
|
| Thickness Increase |
|
| ASTM F146 after immersion in |
|
| ASTM Oil 1, 5h/300°F (149°C) |
0-5% |
| ASTM Oil IRM903, 5h/300°F (149°C) |
0-5% |
| ASTM Fuel A, 5h/73°F (23°C) |
0-5% |
| ASTM Fuel B, 5h/73°F (23°C) |
5-10% |
|
| ASTM F104 Line Call Out |
F712122B3E22M8Z1 |
|
| Leachable Chloride Content |
|
| FSA NMG-202-96 (Typical) |
N/A |
|
| Density |
119 lb/ft3 (1.9 g/cc) |
|
| Color (Top/Bottom) |
Black |
|
Pressure and Temperature
Graphs
Material Thickness: 1/16”
Liquids |
 |
| Gases and Steam |
 |