| Creep Relaxation ASTM F38B (1/32”) |
20% |
|
| Sealability ASTM F37A (1/32”) |
.50 ml/hr |
|
| Klinger Hot Compression Test |
|
| Thickness Decrease 73°F (23°C) |
10% initial |
| Thickness Decrease 572°F (300°C) |
12% additional (480°F/248°C) |
|
| Compressibility ASTM F36J |
7-17% |
| Recovery ASTM F36J |
50% minimum |
|
| Tensile Strength |
|
| ASTM F152 Cross Grain |
1,500 psi typical |
|
| Change in Tensile Strength |
|
| ASTM F152 after immersion in |
25% maximum decrease |
| ASTM Oil IRM903, 5h/300°F (149°C) |
|
|
| Weight Increase |
|
| ASTM F146 after immersion in Fuel B |
15% maximum |
| 5h/73°F (23°C) |
|
|
| Thickness Increase |
|
| ASTM F146 after immersion in |
|
| ASTM Oil 1, 5h/300°F (149°C) |
0-5% |
| ASTM Oil IRM903, 5h/300°F (149°C) |
0-5% |
| ASTM Fuel A, 5h/73°F (23°C) |
0-5% |
| ASTM Fuel B, 5h/73°F (23°C) |
0-5% |
|
| ASTM F104 Line Call Out |
F712121B3E21M5 |
|
| Leachable Chloride Content |
|
| FSA NMG-202-96 (Typical) |
200 ppm |
|
| Density |
119 lb/ft3 (1.9 g/cc) |
|
| Color (Top/Bottom) |
White or Black |
|
Pressure and Temperature
Graphs
Material Thickness: 1/16”
Liquids |
 |
| Gases and Steam |
 |